Magnetization data from CFMS
Sample temperature is Sensor_B_(K)
Magnetic field is B_Analog_(T)
Magnetic moment in emu is moment_(emu)

M(T) files typically start with ZFC warming, then cool back to base T in the same field (FC), then rapidly return to a higher temperature in preparation for the next ZFC run
On warming, there is a broad glitch around 14-15 K where the cooling mode changes.  This is not physically meaningful
There are also several other types of glitch, most notably spikes lasting several data points, or cases (especially in field sweeps) where the program stopped writing data briefly then wrote 2-3 nonsense points at one field before continuing.  These were removed before plotting
The magnet power supply has a discontinuity at ±1.00 T, leading to a small step in the data.  This was not removed for the plots.
Initial measurements in 2024 were supplemented with additional M(H) curves one year later.

The sample mass was 25.454 mg.


Files:

Ktenasite_powder_MT300K_1T.dat		Cooling in 1 T
Ktenasite_powder_MT300K_0p1T.dat	Warming in 0.1 T

Ktenasite_powder_ZFCFC_0p1T.dat		ZFC and FC in 0.1 T
Ktenasite_powder_ZFCFC_0p2T.dat		ZFC and FC in 0.2 T
Ktenasite_powder_ZFCFC_0p5T.dat		ZFC and FC in 0.5 T
Ktenasite_powder_ZFCFC_1T.dat		ZFC and FC in 1 T

Ktenasite_powder_MH_2K.dat		4-quadrant M(H) at 2 K